Ceramic tile sealant is powdered and powdered after seam construction, which is mainly caused by two aspects. First, in the early deployment of ceramic tile sealant paste, excessive water was added, and the composition of ceramic tile sealant binder was diluted by water, which could not form a compact and effective structure, and then appeared powder and powder. Another aspect is the construction of ceramic tile sealant filler, because water retention is a challenge, ceramic tile sealant lacks water hydration hardening reaction, the degree of hydration hardening will be limited, so the hardness and strength of the material will be affected, easy to appear material powder, powder problems.

　　瓷砖填缝施工之前,重要的是,当部署瓷砖填缝剂泥浆,加水太多,也就是说,材料太稀疏,揭或混合材料时,没有使用电动搅拌器,使材料不揭,或者前施工后剩下的瓷砖填缝剂泥浆干,加入水搅拌重用。这三种做法，都会导致瓷砖填充剂出现起粉色、强度差的问题。

　　Before the ceramic tile filling construction, the most important thing is that when the tile filling agent slurry is deployed, too much water is added, that is to say, when the material is too sparse, uncovering or mixing materials, no electric mixer is used to keep the material uncovered, or the remaining ceramic tile filling agent slurry is dry before and after construction, and water mixing is added for reuse. These three methods will lead to the problems of pink and poor strength of ceramic tile filler.

　　另外，瓷砖补缝剂实际上就是补缝施工后的蓄水、保水、保湿、锁水的能力。当砖缝太小时，用瓷砖填充缝剂填充缝隙时，材料的宽度很小，即材料的体积较小。体积小不利于堵缝材料的保水性，易被瓷砖吸收空气中的水分，导致瓷砖堵缝剂粉体问题;此外，瓷砖密封胶填补缝隙，如果填料不饱满、不致密、疏松，瓷砖密封胶之间的缝隙很容易流失水分。这就导致瓷砖填充缝料浆在硬化过程中缺水，容易出现粉状，硬度不够;在如果天气太干太热,瓷砖密封胶施工很容易被吸走空气水分,导致缺乏水淬火条件下,会出现粉、硬度不够,所以当天气热或干燥的天气,喷水维护、合适的润湿材料的一个重要原因。

　　In addition, the ceramic tile sealant is actually the ability to store, retain, moisturize and lock water after the construction of the seam. When the brick seam is too small and the ceramic tile filling agent fills the seam, the width of the material is very small, that is, the volume of the material is small. Small size is not conducive to the water retention of sealing materials, easy to be absorbed by ceramic tiles in the air moisture, leading to the problem of ceramic tile sealant powder; in addition, ceramic tile sealant fills the gap, if the filler is not full, compact, loose, the gap between ceramic tile sealants is easy to lose moisture. This will lead to the lack of water in the hardening process of ceramic tile filling seam slurry, which is easy to appear powdery and hardness is not enough; if the weather is too dry and hot, the construction of ceramic tile sealant is easy to absorb air moisture, resulting in lack of water quenching conditions, there will be powder, hardness is not enough, so when the weather is hot or dry, spray water maintenance, appropriate moistening. An important reason for wet materials.

　　为了防止瓷砖填缝剂发生粉变化,粉红色的情况下,在分配瓷砖填缝剂泥浆在早期,添加水的量要适当,不能太多,当瓷砖填缝剂后的后期建筑保护,水分不能少,应注意材料填满水。

　　In order to prevent the powder change of ceramic tile sealant and pink, in the early stage of distributing ceramic tile sealant slurry, the amount of water should be appropriate and not too much. When the later stage of building protection after ceramic tile sealant, the water should not be less, and the material should be filled with water.

　　以上内容由济南抹面砂浆厂家整理发布，如果您不了解这方面的装饰材料或有产品需求可以点击官网咨询://www.gochiism.com/

　　The above contents are arranged and published by Jinan Gypsum Mortar Manufacturer. If you don't know the decorative materials or product requirements in this area, you can click on the official website to consult: //www.gochiism.com./